Chemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE)

Quantity:
  • Shanghai, China
  • 8000
  • T/T
  • Chemical Storage Tank
  • Horizontal / Vertical
  • Dong Run Ze
  • Nil
  • OEM
  • China
  • 73090000
  • New
  • Customized
  • Metal Tank
  • Horizontal / Vertical
  • Liquid
  • Q235A + PE (Plastic )16mm -22mm
Chemical Storage Tank Customize ( Vertical / Horizontal Acid Storage Tank ) Steel Lined Plastic (LLDPE )Storage Tank For HCl , NaOH (max 50%), NaCLO (max 10%), H2SO4 Chemical Liquid Corrosion Resistance

Steel Lined Plastic LLDPE Vertical Flat Bottom Steel Lined Plastic LLDPE Tank For Storage HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%)
Electrolytic Polishing Tank / Can /Pool Pipe Unit, Electrolytic Cleaning Tank,Acid Polishing Tank



Metal cans Steel-Lined Plastic Square Tank, Electrolytic Tank, Pickling Tank Acid Containment Vessels Custom Made Rotationally Molded Linear Resins LLDPE
Custermizing Checmial Acid Storage Tank 1-150 m3 Steel Lined LLDPE Tank Used to Contain: HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%) , PAC (max 17%) ,H2so4

Used to contain: HCl (max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%), H2SO4 etc


Media (density) : (1155 Kg/m3), Hydrochloric Acid (1150 Kg/m3), Sulfate, Nitrate (1152 Kg/m3), Phosphate (1151 Kg/m3), Hydrofluoric Acid (1132 Kg/m3), Battery Fluid (1135 Kg/m3), Chloride (1135 Kg/m3), Ferric Chloride Solution (1130 Kg/m3), Sodium Hypochlorite (1130 Kg/m3), Sulfurous Acid (1030 Kg/m3)

processing/storing; aluminum sulfate, ammonium sulfate, calcium chloride, ethylene glycol, ferric chloride, ferric sulfate, ferrous sulfate, hydrochloric acid, hydrofluoric acid, hydrofluosilicic acid, hydrogen peroxide, magnesium chloride, phosphoric acid, polymers, potassium hydroxide, or just plain water and we'll design the vessel(s) you require.

Horizontal / Vertical Storage HCL Acid Tanks Steel Lined LDPE
For Storage Bleach, Hydrochloric Acid, Ferric Chloride, Oilfield Chemicals, Corrosive Wastes And Other Hazardous Cargoes.
Steel ( 6 mm -8mm ) Lined PE Plastic 7042 (16mm - 25 mm ) storage tank

Steel Lined LDPE aslo for Steel Lined LDPE Tank aslo for HCL(max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%),H2SO4(60%,98%) ,HF (48%),H3PO4 (10%-85%),NH3. H2O,H2O2 (30%) Hazardous LiquidsTank Container

Steel Lined LDPE aslo for HCL(max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%),H2SO4(60%,98%) ,HF ( 48%),H3PO4 (10%-85%),NH3. H2O,H2O2 (30%)
Compounds, cleaning liquid, UN1760,
Corrosive liquid, acidic, inorganic, n.o.s., UN3264,
Corrosive liquid, acidic, organic, n.o.s., UN3265,
Corrosive liquid, basic, inorganic, n.o.s., UN3266,
Hypochlorite solutions, UN1791,
Hydrochloric acid solution, UN1789,
Sulfuric acid, UN2796,
BATTERY FLUID, ALKALI UN 2797,

Detail Picture

Chemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE) Horizontal Stainless steel Tank Draft Storage 25 m3 (25000L)

Chemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE) Horizontal Carbon steel Tank Draft Storage 5m3 (5000L)
Chemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE) Horizontal Stainless steel Tank Draft Storage 3 m3 (3000L)
Chemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE) Horizontal Stainless steel Tank Draft Storage 1 m3 (1000L)
Chemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE)Horizontal Steel Lined LLDPE Tank Draft Storage 15 m3 (15000L) Bleach
Sodium Hypochlorite , Hydrochloric Acid , other chemical Liquid

Chemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE)
Horizontal Carbon Steel tank Draft Storage 5 m3 (5000L)

Chemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE)
Horizontal Steel Lined LLDPE Tank Draft Storage 10 m3 (10000L) Bleach
Sodium Hypochlorite , Hydrochloric Acid , other chemical LiquidChemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE)
Horizontal Steel Lined LLDPE Tank Draft Storage 1 m3 (1000L) Bleach Sodium Hypochlorite , Hydrochloric Acid , other chemical Liquid

Vertical Bleach Sodium Hypochlorite , Hydrochloric Acid Storage 80m3 (80,000L) Draft
Vertical Bleach Sodium Hypochlorite , Hydrochloric Acid Storage 125m3 (125,000L) Draft
Steel Lined LLDPE Tank

Vertical Bleach Sodium Hypochlorite , Hydrochloric Acid Steel Lined LLDPE Tank Storage 150m3 (150,000L) Draft

Vertical Bleach Sodium Hypochlorite , Hydrochloric Acid Steel Lined LLDPE Tank Storage 100m3 (100,000L) Draft


Vertical Hydrochloric Acid Storage Tanks ,Dosing tank, Day tank 30cbm (30000L) Draft
Vertical Bleach Sodium Hypochlorite , Acid Storage Dosing Tanks 10cbm (10000L) Draft
Vertical Bleach Sodium Hypochlorite , Acid Dosing Tanks , measuring tank 5m3 (5000L) Draft
Vertical Bleach Sodium Hypochlorite , Acid Dosing Tanks , measuring tank 2m3 (2000L) Draft
metering tank Vertical HCl Storage Tanks 90cbm (90000L ,23775Gallon) Draft
Vertical Hydrochloric Acid Storage Tanks 50cbm (50000L) Draft
Vertical Hydrochloric Acid Storage Tanks 30cbm (30000L) Draft
Vertical Hydrochloric Acid Storage Tanks 15cbm (15000L) Draft
Vertical Hydrochloric Acid Storage Tanks 10cbm (10000L) Draft
Vertical Hydrochloric Acid Storage Tanks 5000L Draft

Chemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE)
Chemical Storage Tank Customize 1000L -25000L (Vertical / Horizontal Acid Storage Tank Steel Lined LLDPE)
Concentrated sulfuric acid storage tank
Hydrochloric acid storage tank
Nitric acid storage tank
Sodium hypochlorite storage tank
Ammonia tank
Methanol tank
Hydrogen peroxide storage tank
Sodium hydroxide tank
Storage tank for additives
Polycarboxylic acid storage tank
Urea tank
Rotationally Molded LLDPE TANK
chemical resistance of LLDPE
Cell / :+8615271357675
www.truckinchina.com

LDPE / HDPE Chemical Resistance Chart

The chemical compatibility of LDPE and HDPE on this chart is tested at 20°C: and 50°C: for 7 days and 30 days (if applicable) with constant exposure.

LDPE & HDPE resistance listed by chemical
1.4-dioxane LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows some effect after 7 days.
Acetaldehyde LDPE / HDPE at 20°C: little or no damage after 30 days.
HDPE at 50°C: shows some effect after 7 days.
LDPE at 50°C: immediate damage may occur.
Acetic Acid 5 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Acetic Acid, glacial 50% LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50 °C: immediate damage may occur.
Acetone LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Allyl Alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Aluminum salts LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Amino acids LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonia LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium carbonate saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium phosphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium sulphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Amyl chloride HDPE at 20°C: shows some effect after 7 days.
HDPE at 50°C & LDPE at 20°C-50°C: immediate damage may occur.
Not recommended for continuous use.
Aniline LDPE / HDPE at 20°C: little or no damage after 30 days.
HDPE at 50°C: shows some effect after 7 days.
Benzene LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Benzyl alcohol LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Boric acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Bromine LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Butyric acid LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Calcium chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Calcium hydroxide saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Carbon tetrachloride HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C & HDPE at 50°C: show some effect after 7 days.
LDPE at 50°C: not recommended.
Chlorine 10% in water LDPE / HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 50°C: shows damage and is not recommended.
Chlorobenzene Immediate damage may occur.
Not recommended for continuous use.
Chloroform LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: immediate damage may occur.
Not recommended for continuous use.
Chromic acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Chromic acid 50% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Citric acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Cresol HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage.
Not recommended for continuous use.
Cyclohexane LDPE / HDPE at 50°C: immediate damage may occur.
LDPE / HDPE at 20°C: show some effect after 7 days.
Diethyl ketone LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Dimethylsulfoxide LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethanol 95% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethyl acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethyl benzene HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage.
Not recommended for continuous use.
Ethylene glycol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethylene oxide HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C: and LDPE/ HDPE at 50°C: show some effect after 7 days.
Ferric chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Fluoride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Fluorine HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C: shows some effect after 7 days.
Not recommended at 50°C.
Formaldehyde 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Formaldehyde 40% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Glycerol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hexane HDPE at 20°C: shows little or no damage after 30 days continuous use.
HDPE at 50 °C: shows some effect after 7 days.
LDPE not recommended at any temperature.
Hydrochloric acid 20% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrochloric acid 35% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrochloric acid 5% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrocyanic acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid 4% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid 48% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrogen peroxide 3% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrogen peroxide 30% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Isobutyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Isopropyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Kerosene LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE not recommended at 50°C, as immediate damage may occur.
Lactic Acid 10 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Lactic Acid 90 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Lead acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Methanol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Methyl ethyl ketone Immediate damage may occur.
Not recommended for continuous use.
Methyl propyl ketone HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur.
Not recommended for continuous use.
Methylene chloride HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur.
Not recommended for continuous use.
Mineral oil LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: may show immediate damage and is not recommended.
n-amyl acetate LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows some effect after 7 days or constant exposure.
n-butyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Nitric acid 50 % LDPE at 20°C: shows little or damage after 30 days.
HDPE at 20°C & LDPE at 50°C: show effect after 7 days.
HDPE at 50°C: shows immediate damage and is not recommended.
Nitric acid 70 % LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
n-octane LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Oleic acid HDPE at 20°C-50°C: little or no damage after 30 days.
LDPE at 20°C-50°C: shows immediate damage and is not recommended.
Oxalic acid LDPE at 20°C: shows some effect after 7 days.
HDPE at 20°C and LDPE / HDPE at 50°C: shows little/ no damage after 30 days.
Ozone LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Perchloric acid LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Perchloric ethylene LDPE / HDPE at 20°C-50°C: show immediate damage.
Not recommended.
Phenol LDPE / HDPE at 20°C-50°C: show immediate damage.
Not recommended.
Phosphoric acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Phosphoric acid 85% LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows immediate damage and is not recommended.
Phosphorous trichloride LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: has no data available. HDPE at 50°C: shows some effect after 7 days.
Potassium carbonate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium hydroxide 5 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium hydroxide concentrated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium permanganate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Propylene glycol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Pyridine Immediate damage may occur.
Not recommended for continuous use.
Salicylic acid, saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Silver acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Silver nitrate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium carbonate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium chloride, saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium dichromate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium hydroxide 1% LDPE at 20°C-50°C: shows little or no damage after 30 days.
HDPE at 20°C-50°C: shows some effect after 7 days.
Sodium hydroxide 50% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium hypochlorite 15% HDPE at 20°C-50°C: little or no damage after 30 days.
LDPE at 20°C: is suitable
but at 50°C: shows some effect after 7 days.
Sodium nitrate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium sulphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sucrose LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 20% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 6% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 60% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 98% LDPE at 20°C-50°C: shows little or no damage after 30 days.
HDPE at 20°C: shows effect after 7 days.
Not recommended for use at 50°C.
Tannic acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Tetrahydrofuran LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Toluene LDPE at 20°C: show some effect after 7 day of constant exposure.
HDPE at 20°C-50°C & LDPE at 50°C: show immediate damage.
Not recommended.
Trichloracetic acid LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Trichlorethane Immediate damage may occur.
Not recommended for continuous use.
Turpentine oil LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Urea LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Xylene HDPE at 20°C: shows some effect after 7 day of constant exposure.
LDPE at 20-50°C and HDPE at 50°C: show immediate damage.
Not recommended.
Zinc chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.

Related Products

SUCCESS CASES

More >>

Contact Us

EMAIL:Sale@tictrucks.com
TEL: 86-152-71357675
 WeiChat:king253725877
truck in china weichat made in china truck
 Add:Wuhan Office 1: No.1 Taizong Avenue Gaoqiao Industry Park Taiwanese  Investment Area Dongxihu District Wuhan City, Hubei Province, P.R China
Address CRRC Factory : No. 8 Jiliangdadao,Zengdu Economic Development Zone,Suizhou City, Hubei Province, P.R China P.O. Box 441300  
Address Yuchai DTA Truck Factory : No. 121, Liangshui 1St Road, Zengdu Economic Development Zone Suizhou City, P.R. China  P.O. Box 441300  .......

Hubei Dong Runze Special Vehicle Equipment Co., Ltd. All rights reserved. 2009-2020 XML webmail