EMAIL:Sale@tictrucks.com
TEL:  86-152-71357635    
MOB: 86-152-71357675
ADD: NO.1 TAIZONG AVENUE GAOQIAO INDUSTRY PARK TAIWANESE    INVESTMENT AREA DONGXIHU DISTRICT WUHAN CITY, HUBEI PROVINCE, P.R CHINA
Share to:

Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)

Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)

Quantity:
  • Shanghai, China
  • 3000
  • T/T

Tri Axles Hydrofluoric Acid Tanker Trailer ( Hydrochloride Acid HCL 35% Tank Capacity 33,000L Muriatic Acid )
(3 axles  Semi Trailer 28900Liters,32400liters,33000L Steel Lined LLDPE Acid Tank   WEAK SULFURIC ACID 60% ,20%,6% )  Strong SULFURIC ACID 98% at 20C  degree.
Hydrochloric Acid Tank Semi trailer 3 axles 29900Liters,32400liters
)

Ask for better price

Cell +8615271357675

The pictures are for your reference only.

Hydrochloric acid tank semitrailer 3 axles 29900Liters,32400liters,33800liters

Hydrochloric acid tank semitrailer 2axles 19900Liters,19900Liters,22400liters,23800liters
Tank volume: 22.4 cbm: hydrochloric acid, dilute sulphuric acid ,acetic acid, acrylic acid
tank body effective volume: 23.82 cubic metres,
transport : hydrochloride, hydrogen chlorate, sodium hydroxide,acrylic
acetic acid, glacial acetic acid, hydrogen peroxide

Propionic acid, ammonia,NH3·H2O

Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)
Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)
Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)
Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)

Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)
Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)
Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)


Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)

Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)
Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)
Dangerous Acid Tank Trailer Description of Dilute Sulfuric Acid Tank Trailer Dangerous Acid Tank Trailer The trailer for dilute sulphuric acid transportation is specially designed for the transportation of dilute sulphuric acid. It has a large volume of 22 cmb

Dilute Sulfuric Acid Tank Trailer Dangerous Acid Tank Trailer


Description of Dilute Sulfuric Acid Tank Trailer Dangerous Acid Tank Trailer

The trailer for dilute sulphuric acid transportation is specially designed for the transportation of dilute sulphuric acid. It has a large volume of 22 cmb. In order to ensure safety and stability, the inner lining of the tank is 16 mm thick and the outer layer is made of 6 mm carbon steel, which ensures the safety of transportation.

Even a certain degree of bumping will not lead to tank cracking, and sulfuric acid leakage.

The tank also has a wave-proof plate inside, which reduces the greater pressure caused by starting or braking of the trailer and further strengthens the safety performance of the trailer.


Advantages of Dilute Sulfuric Acid Tank Trailer Dangerous Acid Tank Trailer


Integral Forming

The tank is handled by automatic reeling and rotational moulding. The flange of the nozzle is solid and has to be cut by a puncher. There is no any welded seam in the tank and the lining of the flange. Hence, both the tank and the flange are durable and clean. Any acid or alkali with various concentrations can be resisted.


Waveproof

There are many wave-proof plates inside the tank body, which ensure the safety and stability of the tank body and minimize the impact during start-up and braking.


Specification

Main Dimensions

Overall Dimension

11800x2500x3250

Tare Weight

10900

Loading Capacity

45ton

Tank Body

Shape

Mono block Cylinder

Total Volume (m3)

22cmb

Tanker Body Material

6 mm carbon steel

End Plate

6 mm carbon steel

Inner Lining

16 mm plastics

Manhole Cover

∮500mm;

2 sets with 2 breather valve;

steel manhole cover with plastic lining

Discharging Valve

2 sets ∮100mm discharging valve, stainless made

Safety Valve

1 set of safety valve

Discharging Pipe

4" rubber hose, 2pcs, 6m long

Chassis

Axle

3pcs BPW axle, 13Ton capacity

Landing Gear

JOST brand Two-speed;

manual operating;

heavy duty landing gear

King Pin

JOST brand 2" bolt-in king pin

Suspension

Mechanical suspension with leaf spring

Braking System

WABCO RE 6 relay valve;

T30/30 Spring brake chamber;

40L air tanks

Wheel Rim


9.0-22.5 wheel rim, 12 pieces


Tire

12R22.5 tubeless tire , 12 pieces

Painting

Complete Chassis sand blasting to clean rust,

1 coat of anticorrosive prime, 2 coats of final paint

Accessories

One standard tool box, one spare tyre and carrier

Hydrochloric acid  tank semitrailer 2axles 19900Liters,19900Liters,22400liters,23800liters

Tank volume: 22.4 cbm,

medium: hydrochloric acid, dilute sulphuric acid   (density is 1260 kilograms/cubic meter),

acetic acid, acrylic acid (medium density of 1140   kilograms/cubic meter)


Tank body   effective volume: 23.82 cubic metres,

transport media   name: hydrochloride, hydrogen chlorate, sodium hydroxide,

acrylic (media   density are for 1190 kilograms/cubic metres),

acetic acid,   glacial acetic acid, hydrogen peroxide (media density are for 1140   kilograms/cubic metres)

Propionic acid, (density for   1110 kilograms/cubic metres),

ammonia, (NH3·H2Odensity for 1090 kilograms/cubic metres),

Hydrochloric acid  tank semitrailer 2axles 19900Liters,19900Liters,22400liters,23800liters

Fuwa 13tone axles,

Hydrochloric acid  tank transport semi-trailer


Tri Axles Hydrofluoric Acid Tanker Trailer (Hydrochloride Acid HCl 35% Tank Capacity 33, 000L Muriatic Acid)

Customization, Cost  Control Built How You Want it, at a Price You  Can

Afford. for sale call:+86-152 -7135-7675
chemical resistance of LLDPE   Cell / :+8615271357675  
www.truckinchina.com

LDPE / HDPE Chemical Resistance Chart

The chemical compatibility of LDPE and HDPE on this chart is tested at 20°C: and 50°C: for 7 days and 30 days (if applicable) with constant exposure.

LDPE & HDPE resistance listed by chemical
1.4-dioxane LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows some effect after 7 days.
Acetaldehyde LDPE / HDPE at 20°C: little or no damage after 30 days.
HDPE at 50°C: shows some effect after 7 days.
LDPE at 50°C: immediate damage may occur.
Acetic Acid 5 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Acetic Acid, glacial 50% LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50 °C: immediate damage may occur.
Acetone LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Allyl Alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Aluminum salts LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Amino acids LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonia LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium carbonate saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium phosphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ammonium sulphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Amyl chloride HDPE at 20°C: shows some effect after 7 days.
HDPE at 50°C & LDPE at 20°C-50°C: immediate damage may occur.
Not recommended for continuous use.
Aniline LDPE / HDPE at 20°C: little or no damage after 30 days.
HDPE at 50°C: shows some effect after 7 days.
Benzene LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Benzyl alcohol LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Boric acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Bromine LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Butyric acid LDPE / HDPE at 50°C: immediate damage may occur.
HDPE at 20°C: shows some effect after 7 days.
Calcium chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Calcium hydroxide saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Carbon tetrachloride HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C & HDPE at 50°C: show some effect after 7 days.
LDPE at 50°C: not recommended.
Chlorine 10% in water LDPE / HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 50°C: shows damage and is not recommended.
Chlorobenzene Immediate damage may occur.
Not recommended for continuous use.
Chloroform LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: immediate damage may occur.
Not recommended for continuous use.
Chromic acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Chromic acid 50% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Citric acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Cresol HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage.
Not recommended for continuous use.
Cyclohexane LDPE / HDPE at 50°C: immediate damage may occur.
LDPE / HDPE at 20°C: show some effect after 7 days.
Diethyl ketone LDPE / HDPE at 20°C-50°C: damage may occur.
Not recommended for continuous use.
Dimethylsulfoxide LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethanol 95% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethyl acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethyl benzene HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage.
Not recommended for continuous use.
Ethylene glycol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Ethylene oxide HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C: and LDPE/ HDPE at 50°C: show some effect after 7 days.
Ferric chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Fluoride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Fluorine HDPE at 20°C: shows little or no damage after 30 days.
LDPE at 20°C: shows some effect after 7 days.
Not recommended at 50°C.
Formaldehyde 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Formaldehyde 40% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Glycerol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hexane HDPE at 20°C: shows little or no damage after 30 days continuous use.
HDPE at 50 °C: shows some effect after 7 days.
LDPE not recommended at any temperature.
Hydrochloric acid 20% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrochloric acid 35% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrochloric acid 5% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrocyanic acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid 4% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrofluoric acid 48% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrogen peroxide 3% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Hydrogen peroxide 30% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Isobutyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Isopropyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Kerosene LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE not recommended at 50°C, as immediate damage may occur.
Lactic Acid 10 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Lactic Acid 90 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Lead acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Methanol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Methyl ethyl ketone Immediate damage may occur.
Not recommended for continuous use.
Methyl propyl ketone HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur.
Not recommended for continuous use.
Methylene chloride HDPE at 20°C: shows some effect after 7 days.
LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur.
Not recommended for continuous use.
Mineral oil LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: may show immediate damage and is not recommended.
n-amyl acetate LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows some effect after 7 days or constant exposure.
n-butyl alcohol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Nitric acid 50 % LDPE at 20°C: shows little or damage after 30 days.
HDPE at 20°C & LDPE at 50°C: show effect after 7 days.
HDPE at 50°C: shows immediate damage and is not recommended.
Nitric acid 70 % LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
n-octane LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Oleic acid HDPE at 20°C-50°C: little or no damage after 30 days.
LDPE at 20°C-50°C: shows immediate damage and is not recommended.
Oxalic acid LDPE at 20°C: shows some effect after 7 days.
HDPE at 20°C and LDPE / HDPE at 50°C: shows little/ no damage after 30 days.
Ozone LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Perchloric acid LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Perchloric ethylene LDPE / HDPE at 20°C-50°C: show immediate damage.
Not recommended.
Phenol LDPE / HDPE at 20°C-50°C: show immediate damage.
Not recommended.
Phosphoric acid 10% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Phosphoric acid 85% LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: shows immediate damage and is not recommended.
Phosphorous trichloride LDPE / HDPE at 20°C: little or no damage after 30 days.
LDPE at 50°C: has no data available. HDPE at 50°C: shows some effect after 7 days.
Potassium carbonate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium hydroxide 5 % LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium hydroxide concentrated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Potassium permanganate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Propylene glycol LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Pyridine Immediate damage may occur.
Not recommended for continuous use.
Salicylic acid, saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Silver acetate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Silver nitrate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium carbonate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium chloride, saturated LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium dichromate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium hydroxide 1% LDPE at 20°C-50°C: shows little or no damage after 30 days.
HDPE at 20°C-50°C: shows some effect after 7 days.
Sodium hydroxide 50% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium hypochlorite 15% HDPE at 20°C-50°C: little or no damage after 30 days.
LDPE at 20°C: is suitable
but at 50°C: shows some effect after 7 days.
Sodium nitrate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sodium sulphate LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sucrose LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 20% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 6% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 60% LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Sulfuric acid 98% LDPE at 20°C-50°C: shows little or no damage after 30 days.
HDPE at 20°C: shows effect after 7 days.
Not recommended for use at 50°C.
Tannic acid LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Tetrahydrofuran LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Toluene LDPE at 20°C: show some effect after 7 day of constant exposure.
HDPE at 20°C-50°C & LDPE at 50°C: show immediate damage.
Not recommended.
Trichloracetic acid LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Trichlorethane Immediate damage may occur.
Not recommended for continuous use.
Turpentine oil LDPE / HDPE at 20°C: show some effect after 7 days.
LDPE / HDPE at 50°C: show immediate damage.
Not recommended.
Urea LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.
Xylene HDPE at 20°C: shows some effect after 7 day of constant exposure.
LDPE at 20-50°C and HDPE at 50°C: show immediate damage.
Not recommended.
Zinc chloride LDPE / HDPE at 20°C-50°C: little or no damage after 30 days.


Related Products

SUCCESS CASES

More >>

Contact Us

EMAIL:Sale@tictrucks.com
TEL: 86-152-71357675
 WeiChat:king253725877
truck in china weichat made in china truck
 Add:Wuhan Office 1: No.1 Taizong Avenue Gaoqiao Industry Park Taiwanese  Investment Area Dongxihu District Wuhan City, Hubei Province, P.R China
Address CRRC Factory : No. 8 Jiliangdadao,Zengdu Economic Development Zone,Suizhou City, Hubei Province, P.R China P.O. Box 441300  
Address Yuchai DTA Truck Factory : No. 121, Liangshui 1St Road, Zengdu Economic Development Zone Suizhou City, P.R. China  P.O. Box 441300  .......

Hubei Dong Runze Special Vehicle Equipment Co., Ltd. All rights reserved. 2009-2020 XML Site Map webmail   Made-in-China.com    https://tictrucks.en.made-in-china.com/ 
 www.truckinchina.com ,www.tictrucks.com