Pickling Tank LLDPE Lined Can Customizing For Acid washing Metal Pool (Electrolytic Cell Polishing Metal Tank)
Electrolytic polishing equipment Acid Tank For Metal Dipping
Electrolytic Polishing Tank / Can /Pool Pipe Unit, Electrolytic Cleaning Tank,Acid Polishing Tank
Metal cans Steel-Lined Plastic Square Tank, Electrolytic Tank, Pickling Tank Acid Containment Vessels Custom Made Rotationally Molded Linear Resins LLDPE
Custermizing Checmial Acid Storage Tank 60 m3 Steel Lined LLDPE Tank Used to Contain: HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%) , PAC (max 17%) ,H2so4
Used to contain: HCl (max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%), H2SO4 etc
Media (density) : (1155 Kg/m3), Hydrochloric Acid (1150 Kg/m3), Sulfate, Nitrate (1152 Kg/m3), Phosphate (1151 Kg/m3), Hydrofluoric Acid (1132 Kg/m3), Battery Fluid (1135 Kg/m3), Chloride (1135 Kg/m3), Ferric Chloride Solution (1130 Kg/m3), Sodium Hypochlorite (1130 Kg/m3), Sulfurous Acid (1030 Kg/m3)
processing/storing; aluminum sulfate, ammonium sulfate, calcium chloride, ethylene glycol, ferric chloride, ferric sulfate, ferrous sulfate, hydrochloric acid, hydrofluoric acid, hydrofluosilicic acid, hydrogen peroxide, magnesium chloride, phosphoric acid, polymers, potassium hydroxide, or just plain water and we'll design the vessel(s) you require.
Horizontal / Vertical Storage HCL Acid Tanks Steel Lined LDPE 120000 Liters
For Storage Bleach, Hydrochloric Acid, Ferric Chloride, Oilfield Chemicals, Corrosive Wastes And Other Hazardous Cargoes.
Steel ( 6 mm -8mm ) Lined PE Plastic 7042 (16mm - 25 mm ) storage tank
The chemical compatibility of LDPE and HDPE on this chart is tested at 20°C: and 50°C: for 7 days and 30 days (if applicable) with constant exposure.
LDPE & HDPE resistance listed by chemical | |
1.4-dioxane | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows some effect after 7 days. |
Acetaldehyde | LDPE / HDPE at 20°C: little or no damage after 30 days. HDPE at 50°C: shows some effect after 7 days. LDPE at 50°C: immediate damage may occur. |
Acetic Acid 5 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Acetic Acid, glacial 50% | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50 °C: immediate damage may occur. |
Acetone | LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use. |
Allyl Alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Aluminum salts | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Amino acids | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ammonia | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ammonium carbonate saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ammonium phosphate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ammonium sulphate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Amyl chloride | HDPE at 20°C: shows some effect after 7 days. HDPE at 50°C & LDPE at 20°C-50°C: immediate damage may occur. Not recommended for continuous use. |
Aniline | LDPE / HDPE at 20°C: little or no damage after 30 days. HDPE at 50°C: shows some effect after 7 days. |
Benzene | LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use. |
Benzyl alcohol | LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days. |
Boric acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Bromine | LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days. |
Butyric acid | LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days. |
Calcium chloride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Calcium hydroxide saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Carbon tetrachloride | HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C & HDPE at 50°C: show some effect after 7 days. LDPE at 50°C: not recommended. |
Chlorine 10% in water | LDPE / HDPE at 20°C: shows little or no damage after 30 days. LDPE at 50°C: shows damage and is not recommended. |
Chlorobenzene | Immediate damage may occur. Not recommended for continuous use. |
Chloroform | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: immediate damage may occur. Not recommended for continuous use. |
Chromic acid 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Chromic acid 50% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Citric acid 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Cresol | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage. Not recommended for continuous use. |
Cyclohexane | LDPE / HDPE at 50°C: immediate damage may occur. LDPE / HDPE at 20°C: show some effect after 7 days. |
Diethyl ketone | LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use. |
Dimethylsulfoxide | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ethanol 95% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ethyl acetate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ethyl benzene | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage. Not recommended for continuous use. |
Ethylene glycol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ethylene oxide | HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C: and LDPE/ HDPE at 50°C: show some effect after 7 days. |
Ferric chloride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Fluoride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Fluorine | HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C: shows some effect after 7 days. Not recommended at 50°C. |
Formaldehyde 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Formaldehyde 40% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Glycerol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hexane | HDPE at 20°C: shows little or no damage after 30 days continuous use. HDPE at 50 °C: shows some effect after 7 days. LDPE not recommended at any temperature. |
Hydrochloric acid 20% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrochloric acid 35% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrochloric acid 5% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrocyanic acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrofluoric acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrofluoric acid 4% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrofluoric acid 48% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrogen peroxide 3% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrogen peroxide 30% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Isobutyl alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Isopropyl alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Kerosene | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE not recommended at 50°C, as immediate damage may occur. |
Lactic Acid 10 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Lactic Acid 90 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Lead acetate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Methanol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Methyl ethyl ketone | Immediate damage may occur. Not recommended for continuous use. |
Methyl propyl ketone | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur. Not recommended for continuous use. |
Methylene chloride | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur. Not recommended for continuous use. |
Mineral oil | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: may show immediate damage and is not recommended. |
n-amyl acetate | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows some effect after 7 days or constant exposure. |
n-butyl alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Nitric acid 50 % | LDPE at 20°C: shows little or damage after 30 days. HDPE at 20°C & LDPE at 50°C: show effect after 7 days. HDPE at 50°C: shows immediate damage and is not recommended. |
Nitric acid 70 % | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
n-octane | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Oleic acid | HDPE at 20°C-50°C: little or no damage after 30 days. LDPE at 20°C-50°C: shows immediate damage and is not recommended. |
Oxalic acid | LDPE at 20°C: shows some effect after 7 days. HDPE at 20°C and LDPE / HDPE at 50°C: shows little/ no damage after 30 days. |
Ozone | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
Perchloric acid | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
Perchloric ethylene | LDPE / HDPE at 20°C-50°C: show immediate damage. Not recommended. |
Phenol | LDPE / HDPE at 20°C-50°C: show immediate damage. Not recommended. |
Phosphoric acid 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Phosphoric acid 85% | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows immediate damage and is not recommended. |
Phosphorous trichloride | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: has no data available. HDPE at 50°C: shows some effect after 7 days. |
Potassium carbonate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Potassium hydroxide 5 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Potassium hydroxide concentrated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Potassium permanganate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Propylene glycol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Pyridine | Immediate damage may occur. Not recommended for continuous use. |
Salicylic acid, saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Silver acetate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Silver nitrate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium carbonate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium chloride, saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium dichromate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium hydroxide 1% | LDPE at 20°C-50°C: shows little or no damage after 30 days. HDPE at 20°C-50°C: shows some effect after 7 days. |
Sodium hydroxide 50% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium hypochlorite 15% | HDPE at 20°C-50°C: little or no damage after 30 days. LDPE at 20°C: is suitable but at 50°C: shows some effect after 7 days. |
Sodium nitrate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium sulphate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sucrose | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sulfuric acid 20% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sulfuric acid 6% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sulfuric acid 60% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sulfuric acid 98% | LDPE at 20°C-50°C: shows little or no damage after 30 days. HDPE at 20°C: shows effect after 7 days. Not recommended for use at 50°C. |
Tannic acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Tetrahydrofuran | LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
Toluene | LDPE at 20°C: show some effect after 7 day of constant exposure. HDPE at 20°C-50°C & LDPE at 50°C: show immediate damage. Not recommended. |
Trichloracetic acid | LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
Trichlorethane | Immediate damage may occur. Not recommended for continuous use. |
Turpentine oil | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
Urea | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Xylene | HDPE at 20°C: shows some effect after 7 day of constant exposure. LDPE at 20-50°C and HDPE at 50°C: show immediate damage. Not recommended. |
Zinc chloride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Pickling Tank LLDPE Lined Can Customizing For Acid washing Metal Pool (Electrolytic Cell Polishing Metal Tank)
Electrolytic polishing equipment Acid Tank For Metal Dipping
Electrolytic Polishing Tank / Can /Pool Pipe Unit, Electrolytic Cleaning Tank,Acid Polishing Tank
Metal cans Steel-Lined Plastic Square Tank, Electrolytic Tank, Pickling Tank Acid Containment Vessels Custom Made Rotationally Molded Linear Resins LLDPE
Custermizing Checmial Acid Storage Tank 60 m3 Steel Lined LLDPE Tank Used to Contain: HCl (max 35%) , Naoh (max 50%) , Naclo (max 10%) , PAC (max 17%) ,H2so4
Used to contain: HCl (max 35%), NaOH (max 50%), NaCLO (max 10%), PAC (max 17%), H2SO4 etc
Media (density) : (1155 Kg/m3), Hydrochloric Acid (1150 Kg/m3), Sulfate, Nitrate (1152 Kg/m3), Phosphate (1151 Kg/m3), Hydrofluoric Acid (1132 Kg/m3), Battery Fluid (1135 Kg/m3), Chloride (1135 Kg/m3), Ferric Chloride Solution (1130 Kg/m3), Sodium Hypochlorite (1130 Kg/m3), Sulfurous Acid (1030 Kg/m3)
processing/storing; aluminum sulfate, ammonium sulfate, calcium chloride, ethylene glycol, ferric chloride, ferric sulfate, ferrous sulfate, hydrochloric acid, hydrofluoric acid, hydrofluosilicic acid, hydrogen peroxide, magnesium chloride, phosphoric acid, polymers, potassium hydroxide, or just plain water and we'll design the vessel(s) you require.
Horizontal / Vertical Storage HCL Acid Tanks Steel Lined LDPE 120000 Liters
For Storage Bleach, Hydrochloric Acid, Ferric Chloride, Oilfield Chemicals, Corrosive Wastes And Other Hazardous Cargoes.
Steel ( 6 mm -8mm ) Lined PE Plastic 7042 (16mm - 25 mm ) storage tank
The chemical compatibility of LDPE and HDPE on this chart is tested at 20°C: and 50°C: for 7 days and 30 days (if applicable) with constant exposure.
LDPE & HDPE resistance listed by chemical | |
1.4-dioxane | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows some effect after 7 days. |
Acetaldehyde | LDPE / HDPE at 20°C: little or no damage after 30 days. HDPE at 50°C: shows some effect after 7 days. LDPE at 50°C: immediate damage may occur. |
Acetic Acid 5 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Acetic Acid, glacial 50% | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50 °C: immediate damage may occur. |
Acetone | LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use. |
Allyl Alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Aluminum salts | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Amino acids | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ammonia | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ammonium carbonate saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ammonium phosphate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ammonium sulphate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Amyl chloride | HDPE at 20°C: shows some effect after 7 days. HDPE at 50°C & LDPE at 20°C-50°C: immediate damage may occur. Not recommended for continuous use. |
Aniline | LDPE / HDPE at 20°C: little or no damage after 30 days. HDPE at 50°C: shows some effect after 7 days. |
Benzene | LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use. |
Benzyl alcohol | LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days. |
Boric acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Bromine | LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days. |
Butyric acid | LDPE / HDPE at 50°C: immediate damage may occur. HDPE at 20°C: shows some effect after 7 days. |
Calcium chloride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Calcium hydroxide saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Carbon tetrachloride | HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C & HDPE at 50°C: show some effect after 7 days. LDPE at 50°C: not recommended. |
Chlorine 10% in water | LDPE / HDPE at 20°C: shows little or no damage after 30 days. LDPE at 50°C: shows damage and is not recommended. |
Chlorobenzene | Immediate damage may occur. Not recommended for continuous use. |
Chloroform | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: immediate damage may occur. Not recommended for continuous use. |
Chromic acid 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Chromic acid 50% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Citric acid 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Cresol | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage. Not recommended for continuous use. |
Cyclohexane | LDPE / HDPE at 50°C: immediate damage may occur. LDPE / HDPE at 20°C: show some effect after 7 days. |
Diethyl ketone | LDPE / HDPE at 20°C-50°C: damage may occur. Not recommended for continuous use. |
Dimethylsulfoxide | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ethanol 95% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ethyl acetate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ethyl benzene | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: show immediate damage. Not recommended for continuous use. |
Ethylene glycol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Ethylene oxide | HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C: and LDPE/ HDPE at 50°C: show some effect after 7 days. |
Ferric chloride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Fluoride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Fluorine | HDPE at 20°C: shows little or no damage after 30 days. LDPE at 20°C: shows some effect after 7 days. Not recommended at 50°C. |
Formaldehyde 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Formaldehyde 40% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Glycerol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hexane | HDPE at 20°C: shows little or no damage after 30 days continuous use. HDPE at 50 °C: shows some effect after 7 days. LDPE not recommended at any temperature. |
Hydrochloric acid 20% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrochloric acid 35% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrochloric acid 5% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrocyanic acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrofluoric acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrofluoric acid 4% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrofluoric acid 48% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrogen peroxide 3% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Hydrogen peroxide 30% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Isobutyl alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Isopropyl alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Kerosene | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE not recommended at 50°C, as immediate damage may occur. |
Lactic Acid 10 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Lactic Acid 90 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Lead acetate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Methanol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Methyl ethyl ketone | Immediate damage may occur. Not recommended for continuous use. |
Methyl propyl ketone | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur. Not recommended for continuous use. |
Methylene chloride | HDPE at 20°C: shows some effect after 7 days. LDPE at 20°C-50°C & HDPE at 50°C: Immediate damage may occur. Not recommended for continuous use. |
Mineral oil | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: may show immediate damage and is not recommended. |
n-amyl acetate | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows some effect after 7 days or constant exposure. |
n-butyl alcohol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Nitric acid 50 % | LDPE at 20°C: shows little or damage after 30 days. HDPE at 20°C & LDPE at 50°C: show effect after 7 days. HDPE at 50°C: shows immediate damage and is not recommended. |
Nitric acid 70 % | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
n-octane | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Oleic acid | HDPE at 20°C-50°C: little or no damage after 30 days. LDPE at 20°C-50°C: shows immediate damage and is not recommended. |
Oxalic acid | LDPE at 20°C: shows some effect after 7 days. HDPE at 20°C and LDPE / HDPE at 50°C: shows little/ no damage after 30 days. |
Ozone | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
Perchloric acid | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
Perchloric ethylene | LDPE / HDPE at 20°C-50°C: show immediate damage. Not recommended. |
Phenol | LDPE / HDPE at 20°C-50°C: show immediate damage. Not recommended. |
Phosphoric acid 10% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Phosphoric acid 85% | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: shows immediate damage and is not recommended. |
Phosphorous trichloride | LDPE / HDPE at 20°C: little or no damage after 30 days. LDPE at 50°C: has no data available. HDPE at 50°C: shows some effect after 7 days. |
Potassium carbonate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Potassium hydroxide 5 % | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Potassium hydroxide concentrated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Potassium permanganate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Propylene glycol | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Pyridine | Immediate damage may occur. Not recommended for continuous use. |
Salicylic acid, saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Silver acetate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Silver nitrate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium carbonate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium chloride, saturated | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium dichromate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium hydroxide 1% | LDPE at 20°C-50°C: shows little or no damage after 30 days. HDPE at 20°C-50°C: shows some effect after 7 days. |
Sodium hydroxide 50% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium hypochlorite 15% | HDPE at 20°C-50°C: little or no damage after 30 days. LDPE at 20°C: is suitable but at 50°C: shows some effect after 7 days. |
Sodium nitrate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sodium sulphate | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sucrose | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sulfuric acid 20% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sulfuric acid 6% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sulfuric acid 60% | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Sulfuric acid 98% | LDPE at 20°C-50°C: shows little or no damage after 30 days. HDPE at 20°C: shows effect after 7 days. Not recommended for use at 50°C. |
Tannic acid | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Tetrahydrofuran | LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
Toluene | LDPE at 20°C: show some effect after 7 day of constant exposure. HDPE at 20°C-50°C & LDPE at 50°C: show immediate damage. Not recommended. |
Trichloracetic acid | LDPE / HDPE at 20°C: show some effect after 7 day of constant exposure. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
Trichlorethane | Immediate damage may occur. Not recommended for continuous use. |
Turpentine oil | LDPE / HDPE at 20°C: show some effect after 7 days. LDPE / HDPE at 50°C: show immediate damage. Not recommended. |
Urea | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
Xylene | HDPE at 20°C: shows some effect after 7 day of constant exposure. LDPE at 20-50°C and HDPE at 50°C: show immediate damage. Not recommended. |
Zinc chloride | LDPE / HDPE at 20°C-50°C: little or no damage after 30 days. |
UN3394 T21 TEAL Portable Tank C480S Teal Metal Alkyls Cylinder For KE Materials C-430 Saddle Type Portable Tank , tank capacity 1630L C-480 Saddle Type Portable Tank, tank capacity 1880L YCDT1880-T21 TEAL tank Triethylaluminum (TEAL) Alky Portable Tank Container FOR UN3394 ,UN3399 HS code :8609009000
5 Sets 5-12m3 Lined PTFE / LDPE / PE Circulation Tank Storage Tank Used For Store H2SO4 98% ,75% ,HCL35%,NAOH 45% for Vietnam Chemcial Factory
10pcs Sewer Jetting Nozzles Stainless Steel Ceramic Nozzles 1.5kg To South Africa High-Pressure Cleaning Sewer Drain Jetter Sewer Jetting Nozzel Ceramic Nozzles for Water Jetting Cable 1.5kg-18kg
Inspection company on behalf of TCM for LIWA PLASTICS INDUSTRIAL COMPLEX PROJECT. 10Units T21 TEAL Portable Tank Containers For Metal Alkyls Date : 2021-3-12T21 TEAL tank Triethylaluminum (TEAL) Alky Portable Tank Container tank capacity 1880L FOR UN3394 ,UN3399 HS code :8609009000
16Units UN T21 Portable Tank Container 1880L Cylinder For TEAL Metal Alkyls UN3394 UN3399 Ready to USA T21 TEAL C-430 Tank PROFORMA INVOICE D21080316
20pcs T21 TEAL TANK UN Portable Alkyls 1.88m3 UN3394 Container Ship to Rotterdam After amost 2 and a half months Producing, those 20 units UN Portable T21 TEAL TANK (EMPTY AND NEW TANKS) finally two partial ship From Shanghai Port China To Germany, Transit Through Rotterdam , Country Of Destination Turkmenistan, Transit Through Germany.The commodity is a circulation tare. Temporary bringing in EU. Filling at the Lanxess Organometallics GmbH, Bergkamen, Germany. The end destination - Turkmenistan.
Triethylaluminum (TEAL) Alky Portable Tank Container - tank capacity 1880L - FOR UN3394 ,UN3399 - complete set with valves- full set ADR/RID BV INSPECTION CERTIFICATE BIC Number- Nameplate with individual tank serial number for each tank
5 Sets 5-12m3 Lined PTFE / LDPE / PE Circulation Tank Storage Tank Used For Store H2SO4 98% ,75% ,HCL35%,NAOH 45% for Vietnam Chemcial Factory
16Units T21 TEAL Cylinder Portable Tanks Loading 40GP Containers Delivery to US
Lined PE Mobile Hydrochloric Acid HCl Tank Body 6m3 for Tanker truck lorry SKD Loading
6000Liters Lined PE Mobile Hydrochloric Acid (HCl) Tank For Truck Lorry Ready for Export STEEL SHELL 5MM, HEAD 6MM TANK SIZE :3800*1900*1230MM, OVER ALL SIZE3800*1900*1800MM DISCHARGE VALVE ND80/DN 65
Corrosive Hydrochloric Acid Chemical Liquid Transport Container Trailer Mounted LDPE Liner Steel Tank 25kl Q235 Steel Lining PE Tank capacity: 25000 Liters for transport: HYDROCHLORIC ACID (HCL UN1789)Tank capacity: 25m3
CO FORM B Asia-Pacific Trade Agreement Certificate for 6 Sets Sinotruck HOWO Vacuum Sewer Cleaning Truck and Water Tanker to MONGOLIA SINOTRUCK 4X2 HOWO Combined Sewer Jetting Vacuum Tanker Truck Qty05 SINOTRUCK 4X2 HOWO 6000 Liters water Tanker Truck Qty 01
6 Sets Sinotruck HOWO 8 T Vacuum Jetting Flushing combination Trucks and 6Ton Water Bowser Tanker to MONGOLIA SINOTRUCK 4X2 HOWO Combined Sewer Jetting Vacuum Tanker Truck Qty05 SINOTRUCK 4X2 HOWO 6000 Liters water Tanker Truck Qty 01
Corrosive Hydrochloric Acid Chemical Liquid Transport Container Trailer Mounted LDPE Liner Steel Tank 25kl Q235 Steel Lining PE Tank capacity: 25000 Liters for transport: HYDROCHLORIC ACID (HCL UN1789)Tank capacity: 25m3